Development of a 3D printable maxillofacial silicone: Part I. Optimization of polydimethylsiloxane chains and cross-linker concentration

Research output: Contribution to journalArticle

Original languageEnglish
JournalJournal of Prosthetic Dentistry
DOIs
Publication statusE-pub ahead of print - 4 May 2016

Documents

King's Authors

Abstract

Statement of problem Conventionally, maxillofacial prostheses are fabricated by hand carving the missing anatomic defect in wax and creating a mold into which pigmented silicone elastomer is placed. Digital technologies such as computer numerical control (CNC) milling and 3-dimensional (3D) printing have been used to prepare molds directly or indirectly into which a biocompatible pigmented silicone elastomer is placed. Purpose The purpose of this in vitro study was to develop a silicone elastomer by varying composition that could eventually be 3D printed directly without a mold to create facial/body prostheses. Material and methods The silicone was composed of polydimethylsiloxane (PDMS), filler, catalyst, and cross-linker. Four types of base silicone polymers were prepared with different PDMS molecular weight combinations with long, medium, and short chain length PDMS. The effect of the cross-linker (2.5% to 12.5%) content in these bases was assessed for the effect upon the mechanical properties of the elastomer. Ten readings were made for each formulation, and differences in the means were evaluated with a 2-way ANOVA (α=.05). Results Variations in silicone composition resulted in hardness from 6.8 to 28.5 durometer, tensile strength from 0.720 to 3.524 kNm−1 and tear strength from 0.954 to 8.484 MPa. Significant differences were observed among all formulations (P<.05). These formulations have mechanical properties comparable with the commercial silicones currently used for the fabrication of facial prostheses. The formulation with 5% cross-linker content and high content of long-chain PDMS chains with optimum mechanical properties was chosen for further development. Conclusions The optimum combination of mechanical properties implies the use of one of these formulations for further evaluation in a 3D printer capable of actively mixing and extruding 2-component, room temperature vulcanization silicone.

Download statistics

No data available

View graph of relations

© 2018 King's College London | Strand | London WC2R 2LS | England | United Kingdom | Tel +44 (0)20 7836 5454